Komposisi Kimia Tiub Keluli ASTM A554
| GRED TUBING ASTM A554 | UNS | C | Mn | P | S | Si | Cr | Ni | Mo | Ti | Nota | N |
| ASTM A554 | S30400 | 0.08 | 2 | 0.045 | 0.03 | 1 | 18.0-20.0 | 8.0-11.0 | ||||
| ASTM A554 L | S30403 | 0.035 | 2 | 0.045 | 0.03 | 1 | 18.0-20.0 | 8.0-13.0 | ||||
| ASTM A554 316 | S3160 | 0.08 | 2 | 0.045 | 0.03 | 1 | 16.0-18.0 | 11.0-14.0 | 2.0-3.0 | |||
| ASTM A554 316L | S31603 | 0.035 | 2 | 0.045 | 0.03 | 1 | 16.0-18.0 | 10.0-14.0 | 2.0-3.0 |
Sifat Mekanikal Tiub Keluli A554
| bahan | Haba | Suhu | Kekuatan Tegangan | Kekuatan Hasil | Pemanjangan %, Min |
| Rawatan | Min.º F(º C) | Ksi (MPa), Min. | Ksi (MPa), Min. | ||
| ASTM A554 | Penyelesaian | 1900 (1040) | 75(515) | 30(205) | 35 |
| ASTM A554 L | Penyelesaian | 1900 (1040) | 70(485) | 25(170) | 35 |
| ASME SA554 316 | Penyelesaian | 1900(1040) | 75(515) | 30(205) | 35 |
| ASTM A554 316L | Penyelesaian | 1900(1040) | 70(485) | 25(170) | 35 |
Carta Berat Tiub Keluli ASTM A554
DIMENSI ASTM A554 TIUB MEKANIKAL KIMPALAN DI LUAR DAN DALAM DIAMETER ATAU DINDING
| Saiz OD, in. (mm) | OD, ±dalam. | Mm | ID, ±dalam. | Mm |
| Sehingga 3⁄32 (2.4), tidak termasuk | 0.001 | 0.03 | 0.001 | 0.03 |
| 3⁄32 hingga 3⁄16 (2.4 hingga 4.8), tidak termasuk | 0.0015 | 0.038 | 0.0015 | 0.038 |
| 3⁄16 hingga 1⁄2 (4.8 hingga 12.7), tidak termasuk | 0.003 | 0.08 | 0.005 | 0.13 |
| 1⁄2 hingga 1 (12.7 hingga 25.4), tidak termasuk | 0.004 | 0.1 | 0.006 | 0.15 |
| 1 hingga 11⁄2 (25.4 hingga 38.1), tidak termasuk | 0.005 | 0.13 | 0.007 | 0.18 |
| 1 1⁄2 hingga 2 (38.1 hingga 50.8), kecuali | 0.006 | 0.15 | 0.008 | 0.2 |
| 2 hingga 2 1⁄2 (50.8 hingga 63.5), kecuali | 0.007 | 0.18 | 0.01 | 0.25 |
| 2 1⁄2 hingga 3 1⁄2 (63.5 hingga 88.9), kecuali | 0.01 | 0.25 | 0.014 | 0.36 |
| {{0}}⁄2 hingga 5 (88.9 hingga 127.0), termasuk | 0.015 | 0.38 | 0.02 | 0.51 |
| Lebih 5 hingga 16 (127.0 hingga 406.4), termasuk | 0.00125 in./in. atau mm/mm lilitan-cumference | 0.0013 in./in. atau mm/mm lilitan-cumference |